H11 steel also is called DIN 1.2343 and JIS SKD6 steel. 1.2343 steel is the air-cooling type hot work mold steel. It is one of the three most commonly used of hot work mold steel in the European die-casting industry. The carbide is small and distributed uniformly in steel. H11 tool steel has great cold and heat fatigue resistance, corrosion resistance, hot and cold processing performance and hardenability. It has oxidation resistance, high toughness and wear resistance in the medium temperature. H11 steel round bar sheet plate properties and H11 steel heat treat as below.
1.2343 Steel Characteristics
- The toughness of 1.2343 steel is higher than H13 steel. It needs to heat treatment. And the hardness of general application is 50-54HRC.
- Widely used for the insert parts of the mold.
- High hardness and toughness, meeting many requirements of hot work mold steel.
- The main components are chromium, molybdenum and vanadium, 1.2343 steel is smelted by the electroslag remelting process.
1.2343 Steel Application
The application is decided by DIN 1.2343 steel chemical composition and properties. Some application of 1.2343 steel as below:
- Hot punches
- Forging dies
- Hot shear blades
- Hot gripper dies
- Extrusion tooling
1.2343 tool steel is used for highly stressed structural parts such as aircraft landing gear. And it is suitable for high-speed hammer forging molds. Such as aluminum and magnesium alloy hot forging die, and its hardness always is 42-50HRC. Black metal forging molds, hardness is 40-50HRC. At the situation of hot work die steel with a high risk of cracking, 1.2343 steel is the best choice. The mold useful time that made of 1.2343 steel can be 1.5-3 times that of AISI L6 steel.
H11 Steel Physical Properties
|Density||7.81 g/cm³||0.282 lb/in³|
H11 Steel Mechanical Properties
|Hardness, Rockwell C(air cooled from 982°C, 45 mins)||52.5||52.5|
|Hardness, Rockwell C(air cooled from 1010°C, 45 mins)||56||56|
|Hardness, Rockwell C(air cooled from 1038°C, 45 mins)||57||57|
|Modulus of elasticity||207 GPa||30000 ksi|
|Modulus of elasticity(@538°C/1000°F)||159 GPa||23000 ksi|
|Modulus of elasticity(@204°C/400°F)||190 GPa||27500 ksi|
|Charpy impact(V-notch; air cooled from 1010°C;535°C temper temperature)||13.6 J||10.0 ft-lb|
|Charpy impact(V-notch; air cooled from 1010°C;650°C temper temperature)||27.1 J||20.0 ft-lb|
|Charpy impact(V-notch; air cooled from 1010°C;370°C temper temperature)||33.9 J||25.0 ft-lb|
|Machinability(1% carbon steel)||75.0-80.0%||75.0 – 80.0%|
H11 Steel Grade Equivalent Chart
|Standard||ASTM A681||DIN EN ISO 4957||JIS G4404|
H11 Steel Chemical Composition
|DIN EN ISO 4957||0.28-0.35||0.10-0.40||-||-||0.80-1.20||2.70-3.20||0.40-0.70||-||1.10-1.50|
|JIS G4404||0.32-0.42||Max 0.50||0.03||0.03||0.80-1.20||4.50-5.50||0.30-0.50||1.00-1.50|
H11 Steel Round Bar Plate Sheet Heat Treatment
The machinability rate of 1.2343 tool steels is nearly 75% of that of the W group tool steels.
1.2343 tool steels are formed by using conventional methods, machining and forging.
1.2343 tool steels can be readily welded by conventional methods.
1.2343 tool steels are preheated to 816°C (1500°F). Then the steels are directly heated by increasing the temperature to 1010°C (1850°F) followed by holding for 15 to 40 mins. The steels are then air-quenched.
1.2343 tool steels are forged at 1121°C (2050°F). For this type of steels, forging below 899°C (1650°F) is not preferable.
Cold working may be carried out on 1.2343 tool steels using conventional methods.
1.2343 tool steels are annealed at 871°C (1600°F) and slowly cooled at 4°C (40°F) in the furnace.
Tempering is carried out on 1.2343 tool steels at a temperature ranging from 538 to 649°C (1000 to 1200°F) to obtain Rockwell C hardness of 54 to 38. Double tempering can also be performed in these steels every one hour at the preferred tempering temperature.
1.2343 Steel Quality Certificate
H11 Tool Steel Round Bar Sheet Plate Supply
Specification: Dia Max 800mm; Length: 3000-5800mm
Surface: original black, peeled, polished, machined
Specification: thickness: 16-800mm; width: 205-810mm; length: 3000-5800mm
Surface: original black, machined, polished
We have our own cutting and processing equipment. Specifications can be cut and customized according to your requirements.
We are a professional special steel stockist and supplier with a high-quality stand for many years. As a professional H11 steel supplier, please contacts us for any request of H11/1.2343 steels material. Songshun Steel always with you.
AISI 6150 steel is an alloy spring steel. It has great mechanical properties......
AISI 52100 steel is the representative of high carbon chromium bearing steel type.
4130 alloy steel has high strength and toughness and the hardenability is high.
It has great mechanical property and processability. And it is great choice for the production of the.....
AISI 5140 steel also can be called JIS Scr440 and DIN 1.7035 steel. It is one of the alloy steel.
AISI O2 steel is the better type compare with the O1 tool steel. Its content of carbon, chromium and tungsten has been raised.
M35 steel is high speed tool steel. After the heat treatment, its hardness, red hardness and wear resistance can be.....
12L14 is a free cutting structural steel. And it is easy to be machined.
1045 carbon steel has a tensile strength is 570-700 MPa and Brinell hardness ranging between 170 and 210.
8620 steel is alloy steel and has good strength and toughness properties. This alloy steel is flexible during....
4340 steel has great machinability, heat treatment stability and impact toughness.
4140 steel is an alloy structural steel with high strength, hardenability, good toughness....
T1 HSS tool steel is the most widely used tungsten type of high speed steel. Its properties are great, has good abrasion, toughness and hardness.
M42 high-speed steel is a cobalt-molybdenum tools steel. The addition of 8% cobalt means that M42 has superior red-hardness when....
AISI M2 high-speed steel has largely replaced T1 in most applications due to its superior properties and advantageous pricing. It is a medium....
According to the AISI classification system, chromium hot-work tool steels are designated as group H steels.
The hardness of A2 steel after heat treatment is higher than SKD11 steel. Its hardness could reach 60-62HRC after....